United States Patent O US. Cl. 9648 6 Claims ABSTRACT OF THE DISCLOSURE Vesicular photographic materials comprising a polymeric vehicle and a light decomposable agent. The polymeric material is a mixture of a resin A and a resin B. By adjusting the relative proportions of these resins, the photographic gamma of the film can be altered. The resin A is an ester or acetal of polyvinyl alcohol. The resin B is an epoxy resin, a phenol formaldehyde resin, a urea-formaldehyde resin, a melamine-formaldehyde resin, a cellulose ester, a silicone resin, an isocyanate resin or a copolymer of maleic anhydride with styrene. Preferably, the amount of resin A is at least 50% and the amount of resin B is up to 50% This case is a continuation of application Ser. No. 403,633, filed Oct. 13, 1964.

The present invention relates to photography and, more particularly, to the production of vesicular images.

Vesicular images are formed in a photographic film by small bubbles or vesicles of gas which are formed and trapped in the areas of the film exposed to light and which refract light. Generally speaking, the film has a colloid or a resin coating or vehicle on a backing material and a light-sensitive agent or sensitizer, most commonly a diazo compound, dispersed throughout the coating. When the film is exposed to light, the sensitizer releases molecules of a gas-nitrogen in the case of diazo compounds. These ordinarily do not form vesicles immediately, but they do so when the film is heated, presumably because the vehicle is relaxed sufficiently on heating for the gas molecules to diffuse together into bubbles and for the bubbles to expand. The resulting vesicles make the vehicle opaque to transmission of light in the exposed areas and also reflect and scatter light so that they appear white.

Vesicular photographic materials have been of only limited use in certain applications because of lack of flexibility in the gray scale, or photographic gamma, they possessed. That is, in general it is desirable to reduce the contrast or gamma of light-scattering photographic materials, while in other cases it may be desirable to increase the gamma. It has been known to reduce the photographic gamma while reducing the maximum obtainable density. However, the resultant loss of density range limits the usefulness of this technique.

It also is known to reduce the photographic gamma by treating a vesicular photographic material in a heated aqueous fluid, as is more fully described in copending 3,498,786 Patented Mar. 3, 1970 application Ser. No. 254,560, filed Ian. 29, 1963. This procedure gives good results. However, there is a need for other techniques which avoid the additional process step required.

It is an object of the present invention to provide, in an improved vesicular photographic film, means for adjusting the photographic gamma of the film in which the vehicle is comprised of a blend of two resins to be designated further herein as resin A and resin B. Resin A is a polymer containing an ester or acetal derivative of polyvinyl alcohol; resin B is taken from the group consisting of epoxy resins, phenol formaldehyde resins, urea formaldehyde resins, melamine-formaldehyde resins, celluose esters, such as cellulose acetate butyrate and cellulose nitrate, silicone resins, isocyanate resins, and copolymers of styrene and maleic anhydride.

The ester derivatives are generally obtained by polymerization of esters of vinyl alcohol with aliphatic or aromatic carboxylic acids. The aliphatic acids are preferred, the most suitable being lower fatty and unsaturated acids containing up to about six carbon atoms, such as acetic acid, propionic acid, valeric acid, vinyl acetic acid or crotonic acid. However, higher fatty acids such as octanoic may be used, particularly in combination with lower fatty acids. Suitable aromatic acids include benzoic acid, naphthoic acids and phenyl acetic acid. The ester polymers may be obtained from the monomer by any conventional polymerization method, i.e., bulk, solution or aqueous emulsion or dispersion, in the presence of, e.g., a free radical or ionic catalyst, the detains of which form no part of the present invention.

Polyvinyl acetals are generally made by reaction between aldehydes and polyvinyl alcohol or polyvinyl esters such as polyvinyl acetate. It is preferred that saturated lower aliphatic aldehydes be employed containing up to six carbon atoms, particularly butyraldehyde and formaldehyde. However, small amounts of higher aliphatic aldehydes or aromatic aldehydes such as benzaldehyde may be included. The polyvinyl acetal polymers may contain small amounts of residual hydroxyl groups which have not been converted to the acetal derivative, or of acetate groups which have not been converted to hydrozyl. However, no more than about 60% of the hydroxyl groups, and preferably no more than 25% should remain as free hydroxyl groups, i.e., not converted to a derivative thereof.

It will be appreciated that while the above description of preferred polymers has been directed to homopolymers, copolymers containing more than one acetal, 0r ester group may be used. Thus polyvinyl acetals may contain two or more types of acetal groups or, e.g., acetate units as well as acetal. In addition, relatively minor amounts of other ethylenically unsaturated monomers containing One or more C=C groups may be copolymerized e.g., up to about 5%, as long as the characteristics of the polymer are essentially not altered so as to render it unsuitable.

Epoxy resins which may be used preferably are glycidyl ethers of polyhydric phenols derived by reaction of a polyhydric phenol with epichlorohydrin. For example, one may use the glycidyl ethers of bis phenol A having the formula where n is a number up to about -15. In place of his phenol A, other suitable epoxy resins may be based upon mononuclear diand trihydroxy phenols and other polynuclear polyhydroxy phenols, such as resorcinol, hydroquinone, pyrocatechol, phloroglucinol, bis phenol F, 2,4,4'-trihydroxydiphenyl dimethyl methane,4,4' dihydroxy biphenyl, and the like. In addition, one may use epoxidized unsaturated oils, as described more fully in the Encyclopedia of Chemical Technology, Second Supplement Volume (1960) and other epoxide group-containing materials. However, the glycidyl ethers of his phenol A are preferred and are readily available conimercially.

Phenolic, urea or melamine resins which are used are condensates of a phenol, e.g., phenol and palkyl phenols, melamine or urea with formaldehyde. A wide variety of these materials are known and commercially available. For example, detailed descriptions may be found in the Encyclopedia of Chemical Technology, Volume 1 (1947) pages 741769, and Volume 10 (1953) pages 335368.

The styrene maleic anhydride copolymers may be prepared by any copolymerization system known for these monomers, e.g., bulk, solution or emulsion polymerization in the presence of a catalyst. Lower molecular weight materials are desirable from the standpoint of compatibility and solubility, but higher molecular weight resins also may be used.

The isocyanate resins are isocyanate-ended prepolymers derived by reaction of an excess of polyisocyanate such as tolylene diisocyanate or p,p'-diisocyanatodiphenylmethane with a polyester, polyether or a polyesteramide. Such materials normally are used with additional amounts of polyester, polyether or polyesteramide, and with or without water, in the making of polyurethanes. They are described in prior US. patents and in Polyurethanes, Chemistry and Technology by Saunders and Frisch and Polyurethanes by Bernard A. Dombrow.

The silicone resins, as are known, are polymers in which the repeating units have the formula Rn SIO(4-n) in which R may be alkyl, preferably lower alkyl, e.g., methyl or ethyl, aryl, e.g., phenyl, tolyl, xylyl or naphthyl, aralkyl, e.g., benzyl, alkenyl, e.g., vinyl or allyl, or cycloalkyl, e.g., cyclohexyl. Other groups which may be attached to the silicon atom are hydrogen, ONa, OK, or OR where R has the same meaning as above. As will be appreciated, depending on the value of n in the above formula, the silicone may be linear, branched or cross-linked. For the most part, silicones which are linear or'slightly branched but not extensively cross-linked are preferred because these tend to be more soluble in the organic solvents used in making films. Suitable examples are polysiloxanes, having repeating units of the general formula with end groups such as where R is methyl, ethyl, propyl or vinyl. Detailed descriptions of such polymers may be found, for example, in The Encyclopedia of Chemical Technology, vol. 12, page 393 and An Introduction to the Chemistry of the Silicones by E. G. Rochow, 2d. ed, 1951.

The resins A and B are suitably blended by dissolving in a mutual solvent or by dissolving them in separate solvents and mixing the solutions together. The resulting resin solution is mixed with the sensitizer, preferably first dissolved in a separate solution, and the resulting mixed solution is coated on a substrate and dried, for example, by heating in an oven at 240 F. It will be observed that some of the resins B may be capable of reacting with acetate, hydroxy or acetal groups of resin A. Consequently, a certain amount of cross-linking may take place, e.g., during'this drying step.

After the film is thus prepared, there are at least three different methods of processing it. In one form, the film is exposed to image-forming light, e.g., by being placed in contact with a transparency and exposed to light passing through the transparency. Then, the film is heated to 160300 F. for $5 to 3 seconds. This will produce an image of the opposite photographic sign from the transparency. Thus if the transparency is a negative, a positive vesicular photograph will result.

A second processing system which can be used is first described in US. Patent 2,911,299. In it, the film is exposed to image-forming light and gas released by the sensitizer is allowed to diffuse from the vehicle at a temperature too low for development to take place. Then the film is exposed overall to uniform light, which activates undecomposed sensitizer, and is heated to cause develop ment at 160-300 F. for to 3 seconds, either during or shortly after the second exposure, but before the gas has substantially diffused from the film. This results in image formation in areas not originally struck by light and an image of the same photographic sign as the transparency. Thus a negative transparency results in formation of a negative vesicular photograph which might be called a reversal image or direct image.

The third processing system is that described in US. application Ser. No. 383,169 filed July 16, 1964. In that system, the film is exposed to image forming light of relatively low intensity for at least about 0.5 second and preferably for at least about 2.0 seconds. That is, the light is of low enough intensity that the film does not receive a normal exposure in less than 0.5 second and preferably 2.0 seconds. Then the film receives an overall exposure of light intensity which is sufiicient to expose the film in less than 0.2 second and preferably less than 0.01 second. Overexposure or longer exposure can be tolerated, but there must be sufiicient light to properly expose the film during the indicated time. This procedure avoids a separate diffusion step as used in the method of US. Patent 2,911,299. In some cases, no heating is required to cause development, and the image appears spontaneously. However, in other cases, some heating may be used to advantage, as more fully described in application Ser. No. 383,169.

Any suitable substrate may be employed for the photographic materials. For films, the preferred materials are films of Mylar (polyethylene terephthalate), polyethylene and polypropylene. Paper backings, metal plates and glass slides also are useful for certain applications. Thus, while films are referred to herein, it will be understood that the invention embraces any backing layer.

It has been found that by mixing resins A and B in different proportions it is possible to adjust the photographic gamma of the films and frequently to increase the photographic density. As the amount of the resin B is increased, the degree of change of photographic gamma will generally increase accordingly. The exact proportions used will, of course, vary according to the desired result. For any given pair of resins, it is possible to determine the effect of changes in proportions, making films from them and determining the value of gamma .by conventional sensitometry. A graph is then made in which gamma is plotted as a function of composition, which permits selecting the exact composition for any desired value of gamma. However, in general, the amounts of the resins will fall within the ranges to 50% resin A and to 50% resin B. It also has been found that alterations in the relative amounts of resins A and B change the photographic speed and projection density of the film. In general film speed increases when the contrast is reduced, in a manner somewhat analogous to commercially available silver halide films.

The following examples illustrate the practice of the invention, all parts being by weight.

EXAMPLE I The following constituents were combined with stirring to form a solution:

Parts Butyraldehyde polyvinyl acetal (80% acetal, 0-2.5%

acetate, 17.5-21.0% hydroxyl) 25 General Electric Methylon 75-108 1,4 dioxane 200 p-Diazo N, -N-dimethyl aniline zinc chloride salt 4 Acetonitrile 80 Methvlon 75-108 has the formula 0 OHzCH=OH2 Han.) (0112011) where n=13 The solution was applied to a backing layer of Mylar film and dried. Then the film was exposed to light from a 500 watt tungsten .filament incandescent lamp spaced about 3 inches from the film through an image bearing transparency for twenty seconds and developed by heating for two seconds at 240 F.

An image was obtained which showed a maximum projection density of 2.74.

EXAMPLE II The following constituents were carefully mixed in an open vessel'with stirring continued until a uniform solution was obtained.

. Parts Formaldehyde polyvinyl acetal (50% acetal, 4050% acetate, 5.06.5% hydroxyl) 25 SMA 4000A 1 5 1,4-dioxane 100 p-Diazo, N,N-dimethyl aniline zinc chloride salt 4 Acetonitrile 80 EXAMPLE III Example II was repeated using as the constituents of the solution:

' f Parts Butyraldehyde polyvinyl acetal (88% acetal, 0-2.5%

acetate, 9l3.0% hydroxyl) 25 Resimene 881 1 5 1,4-dioxa'ne 100 p-Diazo N,N-dimethyl aniline zinc chloride salt 4 Acetonitrile 80 A melamine formaldehyde resin composition Type III, 60i2% solids with 20% butanol and 20% xylol having an acid number less than 1 (mg KOH to neutralize 1 g. resin soldid'st) 2a5ndCa)vlscosity L-P (Gardner-Hol'dt bubble tube standar a The image showed a maximum projection density of 2.76.

6 EXAMPLE 1v Example II was repeated, using as the constituents of the solution:

A silicone resin avaialble as an uncatalyzed, light strawcolored solution in xylol containing 60i1% solids, having a specific gravity of 1.06 and a viscosity of 530 c.p.s. (Gardner- Holdt) The image obtained showed a maximum projection density of 2.58.

EXAMPLE V The following materials were combined in parts of acetonitrile to form a solution:

Parts Butyraldehyde polyvinyl acetal 80% acetal, 02.5%

acetate, 180-20% hydroxyl 25 Mondur S 5 1,4-dioxane 180 pDiazo N,N-dimethyl aniline zinc chloride salt 4 Mondur S is a light-colored, stabilized polyisocyanate adduct known for use with polyester resins in the formulation of bake-type one-component room temperaturestable urethane coatings. It has a specific gravity of 1.26-1.28, a total solids content of about available NCO, 1l.513.5% and a softening point of 80l20 C.

The resultant solution was coated on a thin film of Mylar and dried in an oven at 240 F. for 5 minutes. The dried film was placed in contact with a microfilm transparency and exposed to light through the transparency from a mercury arc lamp (General Electric HA4 IT) spaced 2 inches away for 20 seconds. The film was then developed by heating to 240 F. for two seconds.

An image was obtained which showed a maximum projection density of 2.47.

In the following examples, solutions were prepared from the constituents indicated and films were made as described in Example I. Then the films were exposed and A his phenol A-epichlorohydrin condensate by Ciba having a melting point of 130, an epoxide equivalent of 1,785 and a viscosity at 25 C. (Gardner-Holdt) of 2.1.

. The image obtained showed a maximum projection density of 3.00.

EXAMPLE VII Parts Formaldehyde polyvinyl acetal (82% acetal, 9.5-

13.0% acetate, 5.0-6.0% hydroxyl) 25 Uformite 1 -240 5 1,4-dioxane p-Diazo N,N-dimethyl aniline zinc chloride salt 4 Acetonitrile 80 1A. urea-formaldehyde resin available -ln clear, colorless form as 60i2% solids in xylol-butanol (121%) having an ac1d number solids bases 38, specific gravity 1.02, pounds per gallon 8.5, viscosity (Gardner-Holdt at 25 C.) L-Q, mineral thinner tolerance 50 min.

The image obtained had a maximum projection density of 2.75.

EXAMPLE VIII Parts 30% acetate, 5.5-7 hydroxyl) 20 Cellulose acetate butyrate 6 1,4-dioxane 200 p-Diazo N,N-dimethyl aniline zinc chloride salt 4 Acetonitrile 40 The image obtained showed a maximum projection density of 2.34.

EXAMPLE IX Parts Butyraldehyde polyvinyl acetal (80% acetal, -2.5

acetate, l7.5-2l.0% hydroxyl) 25 Nitrocelulose (RS) 3 1,4-dioxane 200 Methyl ethyl ketone 20 p-Diazo N,N-dimethyl aniline zinc chloride salt 4 Acetonitrile 40 The image obtained showed a maximum projection density of 2.74.

Ethyl cellulose can be used in place of nitrocellulose in the above formulation.

EXAMPLE X To illustrate the effect of varying amounts of resins A and B, three films were made according to the method of Examples VI-IX using the following:

Parts Polyvinyl formal 100 Dioxane 480 Dimethylarnino benzene diazonium chloride, boron Acetonitrile 320 Epon 1001 is an epichlorohydrin bisphenol A type epoxy resin having a melting point of 64.76 C. an epoxide equivalent of 450-525, an average molecular weight of 900-1000 and a viscosity of 25 C. (Gardner-Holdt) C-G. Samples of the respective films were exposed on a sensitometer and developed at 240 F. to make a copy of the step wedge of reversed photographic sign. The following results were obtained.

(1) Projection density (f/5 aperture) of 2.0. $2) Projection density (f/5 aperture) of 2.46. 3) Projection density (f/5 aperture) of 2.7.

The photographic contrast (gamma) decreased and the photggrapllilig speed increased progressively from sample 1 t roug EXAMPLE XI The following formulation was used following the method of Example I:

Parts Gelva (M-7, V100R) (polyvinyl acetate copolymer) 25 Methyl ethyl ketone 95 Distilled water 5 General Electric Methylon 75-108 5 p-Diazo N,N-dimethyl aniline zinc chloride salt 4 Acetonitrile 40 The following three formulations were used in making and using films, following the method of Example I:

8 EXAMPLE XII Parts Gelva V-60 v 25 Epon 1001 5 Methyl ethyl ketone p-Diazo-N,N-dimethyl aniline zinc chloride salt 4 Acetonitrile 40 Gelva V-60 is a homopolymer of vinyl acetate supplied in the form of granules whose viscosity is 54-66 cps. in benzene solution containing 86 grams of resin per 1000 ml. of solution, determined at 20 C. with an Ostwald- Cannon-Fenske viscometer, molecular weight (wt. av.) is 300,000, softening point is 385 F. (determined by a modified Kraemer and Sarnow method using 10 grams of mercury over a 6.35 mm. cylindrical plug of Gelva Resin in a 7 mm. diameter glass tube), heat seal temperature is 195 F. (The minimum temperature required for heat sealing of a l-1.5 mil (dry) film cast from methanol solution on ditto paper dried at room temperature for 45 minutes, then force dried for one hour at 70 C. conditioned for 16 hours at 73 F., 50 percent R.H., using a Pack-Rite 1.5 sec. dwell, 10 p.s.i. pressure, on 4" x A" sample, face to face), maximum tensile strength is 6500 p.s.i. (molded specimens2%" gauge x A" x 0.07"conditioned 48 hours at 73 F., 50% RH. Instron Tester at 2 in./min. crosshead speed) percent elongation at yield is 4.8, abrasion resistance is 59 mg. weight loss (Taber abrasion in mg. loss/1000 revs on cast film conditioned 48 hours at 73 F., 50% R.H., C-lO wheels-1000 gm. load), and second order transition temperature is 27 C. 1

EXAMPLE XHI Parts Gelva V100 25 General Electric Methylon 75-108 5 Methyl ethyl ketone 100 p-Diazo-N,N-dimethyl aniline zinc chloride salt 4 Acetonitrile 40 EXAMPLE XIV Pants Gelva V-800 25 Uformite F-240 5 Methyl ethyl ketone 100 p-Diazo-N,N-dimethyl aniline zinc chloride salt 4 Acetonitrile 40 Gelva V-800 is a homopolymer of vinyl acetate suppl ed in the form of granules whose properties, determined by the methods stated in Example XII for Gelva V-60 are as follows: Viscosity, 700-1000 cps.; molecular weight, about 1.5 x10; heat seal temperature,.205-2l5 F.; maximum tensile strength, 7300 p.s.i.; percent elongation at yield, 4.3; abrasion resistance, 59 mg. weigh lOss; second order transition temperature, 29 C.

As can be seen from the forgoing, the vesicular photographic films described herein provide a useful means for controlling sensitivity and the value of gamma. In addition, in the images obtained, the bubbles can be made very small, thereby improving resolution and the bubbles have unusually high stability. Thus it can be seen that these films have many important advantages and achieve the objects of the invention.

The invention has now been described with respect to preferred embodiments, but.it will be appreciated that various changes may be made in the materials used and the details of the processes, and that no limitation thereto s intended, except as the invention is defined in the appended claims. Thus, for example, while particular sensitizers are described in the foregoing examples, any light decomposable solid agent of the type known in vesicular photography may be used, if it is of the type which, upon exposure to light, decomposes into products which are volatile upon warming to form the above-described radiation-scattering discontinuities. The preferred sensitizers are non-reactive to the vehicle and, upon exposure to light, decompose into products which are chemically non-reactive to said vehicle and which are volatile to form radiation-scattering discontinuities only in the light struck areas in said vehicle to thereby furnish a record. Of the preferred sensitizers, those which are especially useful are of the type which decompose to release nitrogen on exposure to light, particularly the diazonium salts. Full descriptions of these sensitizers may be found, for example, in U.S. application Ser. No. 383,169, filed on July 16, 1964, and the prior patents referred to therein, any of the sensitizers disclosed in said application being usable herein.

Similarly other changes may be made in the process such as the kind of light source used, the conditions of development, and the like, within the scope of the invention, since the examples herein are provided only for the purpose of illustration.

We claim:

1. A photographic material capable of furnishing a record solely in the form of a distribution pattern of radiatiomscattering discontinuities formed within an otherwise substantially homogeneous vehicle, said material being in the form of a dry, water-resistant film, the continuous phase of said film being essentially a synthetic, Water-insoluble, non-water swelling mixture of a resin A and a resin B, said mixture containing at least 50% by weight of resin A, said resin A being a polyvinyl alcohol in which at least 40% of the hydroxyl groups are in the form of a member of the group consisting of acetals with aldehydes containing up to about six carbon atoms and esters with an organic carboxylic acid selected from the class consisting of aliphatic carboxylic acids containing up to about six carbon atoms, mixtures thereof with higher aliphatic carboxylic acids, benzoic acid, naphthoic acid and phenyl acetic acid, and said resin B being an epoxy resin and a light decomposable solid agent substantially uniformly dispersed therein as the sole essential decomposable agent, said decomposable agent itself being nonreactive to said vehicle and upon exposure to light decomposing into products which are capable upon warming of forming said radiation-scattering discontinuities only in the light struck areas in said vehicle to thereby furnish said record.

2. A photographic material as set forth in claim 1 in which said resin B is a polyglycidyl ether of a polyhydric phenol.

3. A method of producing a vesicular image which comprises:

exposing to image forming light a vesicular photographic material capable of furnishing a record solely in the form of a distribution pattern of radiation-scattering discontinuities formed within an otherwise substantially homogeneous vehicle, said material being in the form of a dry, Water-resistant, non-water swelling film, the continuous phase of said film being essentially a synthetic, water-insoluble, non-hygroscopic, non-water swelling mixture of a resin A and a resin B, said mixture containing at least 50% by weight of resin A, said resin A :being a polyvinyl alcohol in which at least 40% of the hydroxyl groups are in the form of a member of the group consisting of acetals with aldehydes containing up to about six carbon atoms and esters with organic carboxylic acid selected from the class consisting of aliphatic carboxylic acids containing up to about six carbon atoms, mixtures thereof with higher aliphatic carboxylic acids, benzoic acid, naphthoic acid and phenyl acetic acid and said resin B being an epoxy resin and a light deomposable solid agent substantially uniformly dispersed therein as the sole essential decomposable agent, said decomposable struck areas to thereby furnish said record, and thereafter heating said photographic material to cause development. 4. A method as set forth in claim 3 in which said resin B is a polyglycidyl ether of a polyhydric phenol.

5. A method of producing a vesicular image which comprises:

exposing to image forming light a vesicular photographic material capable of furnishing a record solely in the form of a distribution pattern of radiationscattering discontinuities formed within an otherwise substantially homogeneous, vehicle, said material being in the form of a dry, water-resistant, non-water swelling film, the continuous phase of said film being essentially a synthetic, water-insoluble, non-hygroscopic, non-water swelling mixture of a resin A and a resin B, said mixture containing at least 50% by weight of resin A, said resin A being a polyvinyl alcohol in which at least 40% of the hydroxyl groups are in the form of a member of the group consisting of acetals with aldehydes containing up to about six carbon atoms and esters with organic carboxylic acid selected from the class consisting of aliphatic carboxylic acids containing up to about six carbon atoms, mixtures thereof with higher aliphatic carboxylic acids, benzoic acid, naphtholic acid and phenyl acetic acid and said resin B being an epoxy resin and a light decomposable solid agent substantially uniformly dispersed therein as the sole essential decomposable agent, said decomposable agent itself being non-reactive to said vehicle and upon exposure to light decomposing into products which are chemically non-reactive to said vehicle and which are capable upon warming of forming said radiation-scattering discontinuities only in the light struck areas to thereby furnish said records, diffusing said volatile products from said vehicle without forming an image therein, subjecting said vehicle to substantially uniform irradiation to cause decomposition of an additional quantity of said decomposable agent, and heating said photographic material to cause development and the formation of a vesicular image. 6. A method as set forth in claim 5 in which said resin B is a polyglycidyl ether of a polyhydric alcohol.

References Cited UNITED STATES PATENTS 2,703,756 3/1955 Herrick et al. 96- 91 3,032,414 5/1962 James et al. 9691 3,081,169 3/1963 Parker et al. 9675 3,244,523 4/ 1966 Growold et al. 9675 3,260,599 7/1966 Lokker 9675 FOREIGN PATENTS 850,954 10/1960 Great Britain.

NORMAN G. TORCHIN, Primary Examiner C. BOWERS, Assistant Examiner US. Cl. X.R.

UNITED STATES PATENT OFFICE CERTIFICATE OF CORRECTION Patent No. 3.498.786 Dated Mar. 3, 1970 Inventor(s) Norman T. Notley and Irwin M. Senentz, Jr.

It is certified that, error appears in the above-identified patent and that said Letters Patent are hereby corrected as shown below:

Delete from the heading in Column 1 the words:

"assignors to Kalvar Corporation, New Orleans La. a corporation of Louisiana" Signed and sealed this 13th day of June 1972.

(SEAL) Attest: